Search

Submitted by Fernanda Aparecida Alonge Minutti (fer.alonge@gmail.com) on 2018-05-30T16:01:45Z No. of bitstreams: 1 Fernanda A A Minutti_Dissertação completa_FINAL.pdf: 6994835 bytes, checksum: ab3793efb49bc877a92e10fe9d2d04cd (MD5) Approved for entry into archive by Lucilene Cordeiro da Silva Messias null (lubiblio@bauru.unesp.br) on 2018-05-30T17:03:36Z (GMT) No. of bitstreams: 1 minutti_faa_me_bauru.pdf: 6888158 bytes, checksum: 03946ea4b9fd3ef6aec72596a601b833 (MD5) Made available in DSpace on 2018-05-30T17:03:36Z (GMT). No. of bitstreams: 1 minutti_faa_me_bauru.pdf: 6888158 bytes, checksum: 03946ea4b9fd3ef6aec72596a601b833 (MD5) Previous issue date: 2018-01-24 O presente trabalho apresenta uma alternativa para a minimização do descarte atual, crescente e inadequado do resíduo agronômico pena de galinha (Chicken Feather). Assim, foram estabelecidos parâmetros para gerar um novo produto, painéis de compósitos, com adição de resina ureia-formaldeído, visando verificar as propriedades e possibilidades de aplicação deste produto na construção civil. Ao longo do levantamento bibliográfico, notou-se que a pena de galinha é um tema ainda pouco explorado em pesquisas, traduzindo-se em uma lacuna a ser preenchida. Foi escolhida a resina ureia-formaldeído por ser um componente chave muito utilizado na indústria de chapas particuladas de madeira, o que facilitaria na avaliação comparativa de desempenho do novo compósito. Durante a realização da etapa experimental, constatando-se uma grande dificuldade na trituração das penas, optouse por usá-las inteiras. Ao final desta etapa, a qualidade física das chapas foi insuficiente para a produção dos corpos de prova necessários à realização dos ensaios de caracterização física e mecânica, sendo direcionado aos ensaios de desempenho térmico, para aplicação deste compósito como isolante térmico em edificações. Com a realização destes ensaios, constatou-se o potencial de adequação do material para esta aplicação. Comparados com materiais para isolamento térmico existentes no mercado, os painéis com pena de galinha apresentaram desempenho compatível, bloqueando cerca de 20ºC de temperatura entre uma face e outra. Desta forma, conclui-se que a pena de galinha é um resíduo agronômico com considerável potencial de aproveitamento na produção de painéis, para uso como material isolante térmico em componentes para construção civil. The present work presents an alternative for the minimization of current, increasing and inadequate disposal of agronomic chicken feather residue. Thus, parameters were established to generate a new product, composite panels, with addition of ureaformaldehyde resin, in order to verify the properties and possibilities of application of this product in civil construction. Throughout the bibliographical survey, it was noticed that the feather of chicken is a subject still little explored in researches, translating into a lacuna to be filled. The urea-formaldehyde resin was chosen as a key component widely used in the wood particleboard industry, which would facilitate the comparative evaluation of the new composite performance. During the realization of the experimental stage, it was verified a great difficulty in the crushing of the feathers, it was chosen to use them whole. At the end of this stage, the physical quality of the panels was insufficient for the production of the test specimens necessary for the physical and mechanical characterization tests, being directed to the thermal performance tests, for the application of this composite as thermal insulation in buildings. With the accomplishment of these tests, it was verified the potential of suitability of the material for this application. Compared with existing insulation materials on the market, the panels with chicken feather showed compatible performance, blocking about 20ºC of temperature between one face and another. Thus, it is concluded that the chicken feather is an agronomic residue with considerable potential for use in the production of panels, for use as thermal insulation material in components for civil construction.

The problem of proper disposal of solid waste generated in different industrial processes is one of worldwide environmental concerns nowadays. Thus, this study aimed to establish a new alternative for the disposal of two agro-industrial residues employing them to produce particleboard for different purposes in building construction. The focus was given to the reuse of the sugarcane bagasse (SB) originated during the processing ofSaccharum officinarumfor sugar and ethanol production, and bamboo stem leaves ofDendrocalamus giganteus(BB). For this, six particleboards were produced in the following compositions: with 100% SB, 75% SB + 25% BB, 50% SB+50% BB, 40% SB +60 BB, 25% SB+ 75% BB and 100% BB in the total mass of the composites. The particleboards physical characterization followed Brazilian Standard ABNT NBR 14810-3 to density, moisture content and water absorption. Results showed these raw materials are compatible to particleboard production.

The aim of this research was to produce three-layer Medium Density Particleboard (MDP), with the addition of impregnated paper, in the inner layer, in proportions of 1; 5 and 20%. In this study, MDP was composed with particles of small size in outer layers, and larger particles in internal layer. After panel manufacturing, physical and mechanical tests based on Brazilian Code ABNT NBR 14.810 were carried out to determine moisture content; density; thickness swelling; water absorption; modulus of rupture (MOR) and modulus of elasticity (MOE) in static bending and internal adhesion. Test results were compared to commercial panels, produced with 100% Eucalyptus, considering the requirements specified by Brazilian Code. Properties presented values close to normative specifications, indicating positively the possibility of production of MDP using addition of waste paper impregnated.

This study aimed to investigate physical performance of particleboards produced with waste from sawmills, containing different wood species, and two adhesives: urea-formaldehyde (UF) based resin and castor-oil (PU) based bi-component polyurethane resin. Panels were produced with nominal density 0.8gcm-3; pressing temperature 110°C; pressing time 10 min; specific pressure 5 MPa. Water absorption (2 and 24h); thickness swelling (2 and 24h); density; and moisture content were investigated. Results confirmed that the produced panels presented compatible physical properties in comparison with other researches referred in literature, proving the feasibility of inputs employed. Panels produced PU showed better performance than those produced with UF.

Este trabalho teve como objetivo estudar algumas variáveis de processamento na manufatura de chapas OSB de Pinus taeda. Foram analisados os efeitos: 1) espessura de partículas (0,4, 0,7, 1,0 mm); 2) densidade nominal da chapa (0,65 e 0,90 g/cm3); 3) pressão específica (40, 60, 80 kgf/cm2); 4) tipo de resina (FF, PMUF e MUF); e 5) reforço laminar superficial (lâminas de Pinus taeda). As análises foram baseadas nos resultados das propriedades de flexão estática, ligação interna, absorção de água, inchamento em espessura e taxa de não retorno em espessura. Os resultados demonstraram que 1) a utilização de partículas com 1,0 mm de espessura resultaram em chapas com maior ligação interna; 2) chapas com densidade nominal de 0,90 g/cm3 apresentaram maiores valores de MOE e MOR paralelo e ligação interna; 3) o aumento da pressão especifica não influenciou expressivamente nas propriedades de resistência mecânica e estabilidade dimensional; 4) as chapas produzidas com resina PMUF apresentaram comportamento similar na estabilidade dimensional em relação a resina FF; 5) o reforço laminar superficial aumentou a resistência de MOE e MOR no sentido perpendicular, conferindo melhor balanço estrutural entre as direções paralelo-perpendicular; as médias absolutas indicaram uma tendência de melhora na estabilidade dimensional das chapas.

The main objective of this dissertation is to assess the technical feasibility of the production of mineral boards, through the utilization of Eucalyptus dunnii flake particles of five (5) trees from a plantation located in The Municipal District of Colombo, State of Parana, as well as to value the particles treatments efficiency, the influence of the wood: cement ratio variation and the use of chemical additive. Used cement was commercialy available Portland type. Three particles treatments were analized: (1) particles without treatment; (2) particles treated with hot water for 1 hour at 80 °C; and (3) particles treated with NaOH 1% for 24 hours; with two wood:cement ratios (1:2.5 and 1:3.0) and two chemical additives (CaC12 and MgC12) effects over physical and mechanical properties of pannels. Chemical analysis of samples of all treatments were performed to verify their efficiency. Twelve treatments were generated from the interaction of above mentioned variables, in five panel repetitions which produced a total of sixty (60) paneis. The assessed physical and mechanical properties were: (1) static bending (ME and MR); (2) parailel compression; (3) internal bonding; and (4) dimensional stability (water absorption and thickness swelling after immersion in water). The results were statistically analyzed through factorial analysis of covariance. According to the results of chemical analysis the treatments did not attained their major objectives, which were to reduce the amount of wood extractives, Among the three analyzed factors, particles,. treatments caused a more pronounced effect on the panels properties, with negative contribution in the results. The increment of the wood:cement rate did not showed higher average values for the mechanical properties, except in intemal bonding. In general, MgCl2 was the chemical additive with better performance. The factors interactions showed different influence on the mechanical properties, but analogous influence on the dimensional properties. The combination between wood:cement ratio and chemical additive showed greater influence on MR (Rupture Modulus) and internal bonding . The combinations between particles treatments and chemical additive, particles treatments and wood:cement ratio, showed respectively major influence on ME (Elasticity Modulus) and paraliel compression. Particles treatments and wood:cement ratio interaction affected physical properties in greater degree.

Este trabalho foi desenvolvido com o intuito de avaliar as influencias de diversas variáveis de processamento, geradas devido às diferentes espécies e tipos de partículas utilizadas, sobre as propriedades das chapas. Entre as propriedades, avaliou-se também os efeitos do gradiente vertical de densidade sobre as propriedades mecânicas das chapas, principalmente sobre o MOE e MOR. As espécies utilizadas foram: Pinus taeda3 P. serótina, P. glabra e P.palustris 3 com partículas dos tipos "wafer", "flake" e "sliver". As condições de manufatura das chapas foram: densidade da chapa - 0,75 g/cm3, conteúdo de resina - 8%, umidade das partículas - 5%, temperatura de prensagem - 180°C, tempo de prensagem - 8 minutos, pressão - 40 kg/cm2. A densificação da superfície inferior das chapas foi maior que a da superfície superior. As chapas do tipo "sliver" apresentaram menor densificação superficial que as chapas do tipo "wafer" e "flake", apresentando tendência para formato em "M". Não se pode observar influência de diferentes espécies sobre o gradiente vertical de densidade. As chapas do tipo "wafer" apresentaram maior MOE que as chapas dos tipos "flake" e "sliver", devido principalmente ao maior comprimento das partículas e razão de esbeltez. Nada se pode concluir a respeito dos efeitos da razão de compactação sobre estas propriedades. No MOE pode-se observar também o efeito da maior disponibilidade de resina por unidade de área das partículas, devido ã menor área superficial específica das mesmas. A remoção de uma e duas camadas superficiais afetou os valores do MOE e MOR, principalmente do primeiro, comprovando a influência do gradiente vertical de densidade sobre as mesmas. A razão de planicidade influiu apenas no MOE das chapas. A resistência da ligação interna foi maior para chapas com menor razão de compactação. As chapas do tipo "sliver" apresentaram ligação interna superior ãs chapas dos demais tipos e a causa provável foi a maior densificação da porção média das chapas. A maior disponibilidade de resina por unidade de área das partículas não influiu nesta propriedade. A maior densificação das camadas influiu positivamente na RAP-face. As chapas do tipo "sliver" foram as que apresentaram maior AA e IE nos testes de 2 e 24 horas, e a causa provável deve ser a maior área superficial específica das partículas e menor disponibilidade de resina por unidade de área. O inchamento residual das chapas do tipo "wafer" foi menor que o das chapas dos demais tipos e entre as especies, o P. palustris e P. serótina foram às que apresentaram menor e maior inchamento residual, respectivamente, apresentando relações diretas com IE, comprovando o efeito da menor e maior taxa de liberação das tensões de compressão. Todas as chapas produzidas apresentaram valores de propriedades superiores aos valores mínimos exigidos pela norma americana CS 236-66.

Tests simulating exposure to severe weather conditions have been relevant in seeking new applications for particleboard. This study aimed to produce particleboards with residues of CCB (chromium-copper-boron oxides) impregnated Pinus sp. and castor oil-based polyurethane resin, and to evaluate their performance before and after artificial accelerated aging. Panels were produced with different particle mass, resin content and pressing time, resulting eight treatments. Particles moisture and size distribution were determined, beyond panel physical and mechanical properties, according to NBR14810-3: 2006. After characterization, treatments B and G (small adhesive consumption and better mechanical performance, respectively) were chosen to artificial aging tests. Statistical results analysis showed best performances were achieved for waterproof aged samples, of both B and G treatments. As example, in treatment B, MOR and MOE values were 23 MPa and 2,297 MPa, samples before exposure; 26 MPa and 3,185 MPa, 32 MPa and 3,982 MPa for samples after exposure (non-sealed and sealed), respectively.

Fundação de Amparo à Pesquisa do Estado de Minas Gerais Este trabalho foi dividido em duas etapas: na primeira, painéis OSB foram fabricados com cinco diferentes proporções de misturas entre as partículas de Eucalyptus grandis (Euc) e Pinus elliottii (Pin). Os tratamentos avaliados foram: A, 100% Euc; B, 75% Euc / 25% Pin; C, 50% Euc / 50% Pin; D, 25% Euc / 75% Pin; E, 100% Pin. Na segunda etapa, a proporção entre as espécies foi fixada em 50% e a estrutura do colchão foi alterada, sendo delineados três tratamentos: C, de camadas indistintas; F, formado exclusivamente por partículas de Eucalyptus grandis na face do colchão; e G, formado unicamente com madeira de Pinus elliottii na face. Outra variável avaliada foi a taxa de adesivo: os tratamentos foram aglutinados com 4%, 6% e 8% de sólidos resinosos sobre o peso seco das partículas de um adesivo fenólico com viscosidade de 350 cps, pH 12,15 e 47,63% de sólidos. Foi utilizada parafina em emulsão, na quantidade de 1% em relação ao peso seco das partículas. Para os sete tratamentos, foram feitas 3 repetições, totalizando 63 chapas. As chapas foram submetidas aos testes de flexão estática, ligação interna, arranque de parafuso, expansão linear, inchamento em espessura e absorção de água, obedecendo aos critérios da norma ASTM D 1037-91. Os melhores resultados foram obtidos para as chapas fabricadas com 6 e com 8% de adesivo; porém, a maioria dos resultados obtidos com painéis produzidos com 4% de adesivo foi superior ao mínimo exigido pela norma CSA O437-93. Os painéis fabricados com 50% de cada espécie alcançaram valores satisfatórios. Nenhum tratamento teve êxito ao ser avaliado para inchamento em espessura; entretanto, todos foram aprovados no teste de expansão linear. Não houve diferença estatística entre as estruturas de colchão avaliadas. This work has been divided into two steps: in the first one, OSB was produced from five mixtures of Eucalyptus grandis (Euc) and Pinus elliottii (Pin). The treatments evaluated were: A: 100% Euc, B: 75% Euc / 25% Pin, C: 50% Euc / 50% Pin, D: 25% Euc / 75% Pin, E: 100% Pin. In the second step, the parcel of each specie was set in 50% and the mat structure was modified, so that three treatments were designed: C, with indistinct layers; F, with only Eucalyptus grandis in the mat faces; and G, with only Pinus elliottii in the mat faces. A phenolic resin containing 47,63% of total solids, pH of 12,15 and viscosity of 350 cps was used as an adhesive, with three levels of 4%, 6% and 8% of resin solids based on the oven-dry weight of particles. One per cent of wax emulsion was also added. Each treatment was replicated three times. Sixty-three boards were produced. The following properties were determined: static bending (MOR and MOE), internal board, screw withdrawal, thickness swelling, water absorption and linear expansion, following the ASTM D 1037-91 procedures. In general, the best results were observed on boards made with 6 and 8% of resin. But most treatments carried out with 4% of adhesive achieved the mechanic tests requirements of the CSA O437-93 standard. The best results were observed on boards fabricated with 50% of each species. No treatment was successful in thickness swelling. On the other hand, all treatments showed satisfactory results in linear expansion. No statistical difference has been found between the mat structures evaluated.

Made available in DSpace on 2016-03-02T13:03:13Z (GMT). No. of bitstreams: 0 Previous issue date: 2014. Added 1 bitstream(s) on 2016-03-02T13:14:39Z : No. of bitstreams: 1 ISSN2317-3009-2014-03-2014-20.pdf: 312609 bytes, checksum: 2f89a8f09ccdbb79963dd599f35e7d39 (MD5) A produção de produtos derivados de madeira e bambu vem crescendo nos últimos anos na busca de um aproveitamento mais racional dessas matériasprimas. Este trabalho tem por finalidade, o estudo da aplicação de resíduos do processamento do café em um painel MDP. Os painéis MDP foram produzidos com partículas de bambu da espécie Dendrocalamus giganteus e adição de partículas de casca de café na camada intermediária do painel, unidas por resina poliuretana à base de mamona. A caracterização físico-mecânica foi realizada baseando-se nas especificações da NBR 14810-3 (2006). Os resultados obtidos foram comparados com a norma brasileira NBR 14810-2 (2006), resultando em valores próximos aos comercialmente encontrados. Universidade Estadual Paulista Júlio de Mesquita Filho, Faculdade de Engenharia de Bauru, Bauru, Av. Eng. Luiz Edmundo C. Coube, 14 -01, Vila Universitária, CEP 17033360, SP, Brasil Universidade Estadual Paulista Júlio de Mesquita Filho, Faculdade de Engenharia de Bauru, Bauru, Av. Eng. Luiz Edmundo C. Coube, 14 -01, Vila Universitária, CEP 17033360, SP, Brasil